SEBS_PP热塑性弹性体的制备与性能研究

SEBS_PP热塑性弹性体的制备与性能研究

理论与研究

文章编号：1005-3360（2009）06-0023-04

SEBS/PP热塑性弹性体的制备与性能研究

Study on the Performance of SEBS/PP Thermoplastic

Elastomer and Its Preparation

吴盾，刘春林(1)，张兰芬，李军 Huang Renjun, Wu Dun, Liu Chunlin(1), Zhang Lanfen, Li Jun

SEBS_PP热塑性弹性体的制备与性能研究

黄仁军，

- 江苏工业学院材料科学与工程学院，江苏常州 213164

- Department of Materials Science and Engineering, Jiangsu Polytechnic University, Changzhou 213164, China

摘　要 :

以苯乙烯-乙烯-丁二烯-苯乙烯嵌段共聚物（SEBS）和聚丙烯（PP）为基体树脂，以碳酸钙（CaCO3）为填充材料，用氢化白油调节其硬度及加工流动性，在一定的工艺条件下添加助剂用开炼机混炼制备SEBS/PP热塑性弹性体；研究了氢化白油、CaCO3和热塑性弹性体等对SEBS/PP共混体系性能的影响。used hydrogen oil for improving the stiffness and fluidity, and used calcium carbonate as filler, with another assistants mixed by mixing mill at definite technological conditions, the SEBS/PP thermoplastic elastomer was prepared. The effects of hydrogen oil, calcium carbonate and thermoplastic elastomer on the performances of SEBS/PP were investigated.

Abstract : Based on the resin styrene-ethylene-butadiene-styrene (SEBS) and polypropylene(PP), which

关键词 : 苯乙烯-乙烯-丁二烯-苯乙烯；聚丙烯；氢化白油；热塑性弹性体中图分类号 :TQ325.14文献标识码 : A

Key words : SEBS; Polypropylene; Hydrogen white oil; Thermoplastic elastomer

SEBS是一种用途广泛的新型热塑性弹性体，

是由热塑性嵌段共聚物苯乙烯-丁二烯-苯乙烯(SBS)分子中丁二烯段不饱和双键经过选择加氢而制得的新型改性弹性体[1]。SEBS是热塑性材料，在常温下具有橡胶的高弹性，在高温下可以熔融流动，直接加工成型，又由于其丁二烯段不饱和双键被加氢饱和使之获得了较其他弹性体更为优异的性能，如优异的耐臭氧、耐氧化、耐紫外线和耐候性能等。SEBS的应用范围远远广于普通SBS，自80年代初正式工业化以来，其一直是国际上公认的用我国起途广泛的新型弹性体材料[2-4]。在这方面，步较晚，本实验就是基于这点对SEBS的应用改性进行研究，以供参考。

乙烯丙烯酸共聚物(EAA)，美国陶氏化6 100，学公司；

乙烯丙烯酸甲酯共聚物（EMA），杜邦公司；1 209，上海慧盟贸易有限公司。SEBS-g-MAH，1 901，

1.2 仪器与设备

双辊开炼机，上海橡胶机械厂；SK-160B，平板硫化机，常州市第一XLB-D350×350×2，橡塑设备厂；

熔体流动速率测试仪，深圳新三思ZRZ1402，

材料检测有限公司；

电子万能试验机，深圳市凯强利机械WDT-5，有限公司；

邵氏硬度计，上海材料试验机厂。XHR-150，

1 实验部分

1.1原料与助剂

巴陵石油化工有限责任公司；SEBS，YH-602，

市售；氢化白油，15#，，市售；重质碳酸钙（CaCO3）1 250目，聚丙烯（PP），金陵石油化工有限责任公司；045-2，